6061-T6 Aluminium specifications: what the numbers mean
6061-T6 Aluminium is a heat treatable aluminium alloy with magnesium and silicon, in the T6 temper. It is used for general machined parts where weight, strength and cost have to be balanced. This entry explains what it is, what the numbers on a data sheet mean, and what to put on a drawing.
It is written from the point of view of the buyer and the drawing office: the values that are realistic in production, the ones that cost money, and the way the result is verified. Where an industry sets the requirement, robotics is used as the example: repeatability across a family of near identical parts.
What the numbers mean
A data sheet for 6061-T6 Aluminium is only useful if the numbers are read against the job. The usual entries, and what they tell you, are these.
- Tensile strength – 310 MPa.
- Yield strength – 276 MPa.
- Hardness – 95 HB.
- Density – 2.70 g/cm³.
- Machinability – good, with a built up edge at low speed.
- Weldability – good, with a loss of strength in the heat affected zone.
Comparing offers
Two suppliers can quote the same tensile strength and mean different things, because the figures are often quoted under the most favourable conditions. Ask what the value is measured over, what the material was, and whether it is a typical or a guaranteed figure.
| Specification | Typical value |
|---|---|
| Tensile strength | 310 MPa |
| Yield strength | 276 MPa |
| Hardness | 95 HB |
| Density | 2.70 g/cm³ |
| Machinability | good, with a built up edge at low speed |
| Weldability | good, with a loss of strength in the heat affected zone |
What to check before specifying
Make sure the value you need is the value you have called up. Use it as the default for any part that does not need higher strength, and the difference between a typical and a worst case figure is where most disputes start.
Applications
6061-T6 Aluminium is used for general machined parts where weight, strength and cost have to be balanced, and in practice it appears most often in enclosures, brackets, heat sinks, machine frames.
How it fits into a machining route
6061-T6 Aluminium is chosen at the drawing stage, and everything downstream follows from it: the tool geometry, the cutting data, the heat treatment and the certificate. Changing the grade later is a different part, not a different quote.The route is fixed before the first part is cut, and it is the route rather than the individual setting that holds the result: material cost is low, so the process dominates. Where a drawing calls for something the route cannot hold economically, that is raised at quotation rather than after the parts are made.
Standards, documentation and what is issued
The documentation requirement is EN 10204 3.1 available on request. Material is supplied against a certificate where the application calls for it, inspection results are recorded with the job, and the records are kept so that a repeat order can be compared with the first instead of being measured from scratch.
Standard dimensional inspection is the verification step. Where a customer format or a standard report is required, it is agreed before the batch starts, because a report written after the event is a report nobody can use.
Frequently asked questions
What tolerance should be specified for 6061-T6 Aluminium?
±0.02 mm is realistic in production. Tightening it beyond the functional requirement increases cost without improving the part.
Which material is usually used?
6061-T6 aluminium is the usual choice, supplied against EN 10204 3.1 available on request.
How is the result verified?
Standard dimensional inspection, with the results recorded so a repeat order can be compared with the first.
What is the most common mistake?
Calling up a hard anodise on a part with tight tolerances, because the coating builds up.
How long does it take and what does it cost?
A realistic cycle is fast cutting, low tool wear, and the cost driver is material cost is low, so the process dominates.
Related capability
If you are specifying 6061-T6 Aluminium on a drawing and want a second opinion on the route, send the model and the quantity. The first response is a manufacturability review with the likely risk points and a quotation, so the decision can be made on facts rather than on a price alone.
Machining, inspection and documentation are handled in one place, which is why the dimensional report and the material certificate arrive with the parts rather than after them.